600mm alta potentia graphite electrode
Gradus: High Power
Fornax applicabilis: EAF
Longitudo: 2100mm/2400mm/2700mm
Papilla: 3TPI/4TPI
Payment: T/T, L/C
Shipping Term: EXW/FOB/CIF
MOQ:10TON
| Comparison Technical Specification for HP Graphite Electrode 24″ | ||
| Electrode | ||
| Item | Unitas | Supplementum Spec |
| Typica Characteres Poli | ||
| Nominal Diameter | mm | 600 |
| Max Diameter | mm | 613 |
| Min Diameter | mm | 607 |
| Longitudo nominal | mm | 2200-2700 |
| Max Longitudo | mm | 2300-2800 |
| Min Longitudo | mm | 2100-2600 |
| mole Density | g/cm3 | 1.68-1.72 |
| vires transversales | MPa | ≥10.0 |
| Iuvenis Modulus | GPa | ≤12.0 |
| Imprimis resistentia | µΩm | 5.2-6.5 |
| Maxime current density | KA/cm2 | 13-21 |
| Current Capacitas baiulans | A | 38000-58000 |
| (CTE) | 10-6℃ | ≤2.0 |
| cinis contentus | % | ≤0.2 |
| Notae typicae Papillae (4TPI/3TPI) | ||
| mole Density | g/cm3 | 1.78-1.83 |
| vires transversales | MPa | ≥22.0 |
| Iuvenis Modulus | GPa | ≤15.0 |
| Imprimis resistentia | µΩm | 3.2-4.3 |
| (CTE) | 10-6℃ | ≤1.8 |
| cinis contentus | % | ≤0.2 |
Cum cupro, graphite commoda habet ut minus consummatio, celerius missionem rate, leviore pondere et minore coëfficiente expansione scelerisque, ita sensim electrode aeris substituit ut amet materias missionis processus efficiat.Secundum capacitatem fornacis electricae, electrodes graphitae diversarum diametrorum adhibentur.Pro continuo usu electronicorum, electrodes per iuncturam electronicorum filamentis connexae sunt.Electrodes graphites usus est in ferro rationem reddendi circiter 70-80% totius consumptionis electrodes graphitae.
Graphite electrode consumptio et fractio communis in usu est.Quas istas causas?Hic est analysis pro relatio.
| factores | Corpus Breakage | Papilla Breakage | solvens | Spalling | Electtode Loss | Oxidation | Electorde Consummatio |
| Non ductores in crimen | ◆ | ◆ |
|
|
|
|
|
| Gravis exiguo in crimen | ◆ | ◆ |
|
|
|
|
|
| Transformer overcapacitatem | ◆ | ◆ |
| ◆ | ◆ | ◆ | ◆ |
| Tres tempus iniquitate | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Phase gyrationis |
| ◆ | ◆ |
|
|
|
|
| Nimia Vibratio | ◆ | ◆ | ◆ |
|
|
|
|
| Clamper Pressura | ◆ |
| ◆ |
|
|
|
|
| Tectum electrode tabernaculi non apponunt cum electrode | ◆ | ◆ |
|
|
|
|
|
| Aqua frigida iniecto super tectum electrodes |
|
|
|
|
|
| △ |
| Scrap preheating |
|
|
|
|
|
| △ |
| Secundarium voltage Excelsa | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Secundarium vena nimis alta | ◆ | ◆ |
| ◆ | ◆ | ◆ | ◆ |
| Potestas preme | ◆ | ◆ |
| ◆ | ◆ |
| ◆ |
| Oleum consummatio nimis |
|
|
| ◆ | ◆ |
| ◆ |
| Consummatio Oxygeni nimis alta |
|
|
| ◆ | ◆ |
| ◆ |
| longum tempus calefactio |
|
|
|
|
|
| ◆ |
| Electrode tingens |
|
|
|
| ◆ |
| ◆ |
| Sordida nexum partem |
| ◆ | ◆ |
|
|
|
|
| Pauperem sustentationem ad levare plugs et constringendos instrumenta |
| ◆ | ◆ |
|
|
|
|
| Satis nexum |
| ◆ | ◆ |
|
|
|
|
pro bono factores
stat ad esse malum factores