UHP 550mm Graphite Electrode
Graphitization est scaena maximi momenti in productione graphitica electrode UHP. Indicat summus calor caloris tractandi processum carbonis productorum supra MMCCC in fornace electrici summus temperatus ut structuram carbonis in tria dimensiva graphite crystalli graphite ordinatam structuram tenebrarum amorphos convertat.
Quid funiculus graphitizationis?
* Amplio electrica ac scelerisque conductivity
*Resistentiam scelerisque inpulsam et stabilitatem chemicam emendare (expansio linearis coefficiens per 50-80% reducitur);
*Fac materia carbonis levitatem et resistentiam habent;
* Impuras dimitte et puritatem materiae carbonis (contentum cineris producti minuitur ab 0.5% ad fere 0.3%).
| Comparison Technical Specification for UHP Graphite Electrode 22" | ||
| Electrode | ||
| Item | Unitas | Supplementum Spec |
| Typica Characteres Poli | ||
| Nominal Diameter | mm | 550 |
| Max Diameter | mm | 562 |
| Min Diameter | mm | 556 |
| Longitudo nominal | mm | 1800-2400 |
| Max Longitudo | mm | 1900-2500 |
| Min Longitudo | mm | 1700-2300 |
| mole Density | g/cm3 | 1.68-1.72 |
| vires transversales | MPa | ≥12.0 |
| Iuvenis Modulus | GPa | ≤13.0 |
| Imprimis resistentia | µΩm | 4.5-5.6 |
| Maxime current density | KA/cm2 | 18-27 |
| Current Capacitas baiulans | A | 45000-65000 |
| (CTE) | 10-6℃ | ≤1.2 |
| cinis contentus | % | ≤0.2 |
| Notae typicae Papillae (4TPI) | ||
| mole Density | g/cm3 | 1.78-1.84 |
| vires transversales | MPa | ≥22.0 |
| Iuvenis Modulus | GPa | ≤18.0 |
| Imprimis resistentia | µΩm | 3.4～3.8 |
| (CTE) | 10-6℃ | ≤1.0 |
| cinis contentus | % | ≤0.2 |